MCON Steel ARP

MCON Steel ARP

MCON STEEL ARP is a single part zinc rich primer, which can be applied on a steel or galvanized or concrete surface to protect the surface from weathering & chemical resistance. Typical Properties Drying Time: Surface dry in 30 to 60 minutes Dry Film Thickness: 150 microns per coat Basic Binder: Acrylic Polymer Gloss: Low Packing: 5 kgs. pack Coverage: 10 to 12 m2 per pack of 5 kgs.

MCON STEEL ARP is a single part zinc rich primer, which can be applied on a steel or galvanized or concrete surface to protect the surface from weathering & chemical resistance. Metallic Zinc imparts cathodic protection to the base metal. It resists photo degradation by UV light as it contains UV absorber. MCON STEEL ZRP has high zinc content to provide steel with protection of undercoating.

Areas of Application
Structural steel and piping exposed to a wide range of corrosive atmospheric environments up to very high. Recommended for offshore environments, refineries, power plants, bridges, buildings, mining equipment and general structural steel.

Advantages
High solids ensures better protection
High zinc content for the best of anti corrosion properties
Designed for severe corrosive environments
The product conforms to the compositional requirements of SSPC paint 20, level 2 and ISO
12944/ISO 20340 and the zinc pigments comply with ASTM D520 type II zinc dust.
UV Resistance – It has excellent UV resistance and adhesion.
New binder technology shows superior performance in adhesion/cohesion
Factory made product with consistent quality.
Fast dry-to-recoat and dry-to-handle

Specification

Typical Properties

Drying Time: Surface dry in 30 to 60 minutes
Dry Film Thickness: 150 microns per coat
Basic Binder: Acrylic Polymer
Gloss: Low
Packing: 5 kgs. pack
Coverage: 10 to 12 m2 per pack of 5 kgs.

 

Direction for use

Remove oil, grease and other contaminants using proper degreasing agent. For severe corrosive conditions blast clean the surface. Special care must be taken on weld areas to remove flux & spatter. The cleaned surface should be coated before it gets contaminated or applies wash primer before subsequent coat of zinc rich primer. Stir base thoroughly then mix three parts base and one part hardener by volume to uniform consistency. Allow the mixture to mature for 20-30 min. and stir again before application & occasionally during use to prevent setting of metallic zinc. For Brush Roller,Airless spray application, no thinning is required. In conventional spraying, 5 % to 10 % thinning is recommended for ease of application.

 

Coverage

5 kg MCON STEEL ARP covers 10 to 12 m2 per pack

6 to 8 hrs after completion of first coat, take up second coat application in a direction perpendicular to the first.

MCON STEEL 2K will dry in 20 minutes however it takes 24 hours to cure. Application of a second coating will ensure proper rust protection.

 

Packaging

1 kg, 5 kgs

 

Storage and Shelf life

Store away from direct sunlight. 12 months from date of manufacture